很多种类的产品模具在制造加工的过程中抛光工作要做的非常的到位，这样才能对模具的质量产生好的影响，那么模具的抛光会受哪些因素的影响呢？
Many kinds of product molds in the process of manufacturing and processing polishing work to do very in place, so as to have a good impact on the quality of the mold, so the polishing of the mold will be affected by what factors?
模具抛光不仅能满足产品外观光泽度的要求，同时还能改善产品的耐腐蚀性和耐磨性。所以模具抛光对产品是有实质性的好处的。
山东模具制造厂家认为如果热处理不当，钢材表面硬度不均或特性上有差异，会给抛光造成困难。
Die polishing can not only meet the requirements of gloss, but also improve the corrosion resistance and wear resistance of products. So die polishing is of substantial benefit to the product. Shandong mold manufacturers believe that if improper heat treatment, uneven hardness of steel surface or differences in characteristics, will cause difficulties to polishing.
优质的钢材是获得良好抛光质量的前提条件，钢材中的各种夹杂物和气孔都会影响抛光效果。要达到良好的抛光效果，工件必须在开始机械加工时要注明抛光的表面粗糙度，当一件工件确定需要镜面抛光时，必须要选抛光性能好的钢材并且都经过热处理否则达不到预期的效果。
High quality steel is the prerequisite to obtain good polishing quality. Various inclusions and pores in steel will affect the polishing effect. In order to achieve good polishing effect, the workpiece must be marked at the beginning of the machining surface roughness, when a workpiece is determined to mirror polishing, must be selected with good polishing performance of steel and heat treatment or not to achieve the desired effect.
由于抛光主要是靠人工完成，所以人的技能目前还是影响抛光质量的主要原因。一般认为抛光技术影响表面粗糙度，其实好的抛光技术还要配合优质的钢材以及正确的热处理工艺，才能得到满意的抛光效果；反之，抛光技术不好，就算钢材再好也做不到镜面效果。
Since polishing is mainly done manually, human skills are still the main reason for affecting the quality of polishing. It is generally believed that polishing technology affects surface roughness. In fact, good polishing technology should be matched with high quality steel and correct heat treatment process to obtain satisfactory polishing effect. On the contrary, the polishing technology is not good, even if the steel is good, it can not do the mirror effect.
材料在机械加工过程中，表层会因热量、内应力或其他因素而损坏，切削参数不当会影响抛光效果。电火花加工后的表面比机械加工或热处理后的表面更难研磨，因此电火花加工结束前应采用电火花精修整，否则表面会形成硬化薄层。
Material in the process of mechanical processing, the surface will be damaged by heat, internal stress or other factors, improper cutting parameters will affect the polishing effect. Edm surfaces are more difficult to grind than machined or heat treated surfaces, so edM finishing should be used at the end of edM, otherwise the surface will form a hardened thin layer.
The polishing of the mold will be affected by a number of factors related content is the above, if you have questions about this aspect might as well come to our www.sdlqmj.com website to discuss.